Effect of temperature on the passive state of Alloy 31 in a LiBr solution: Passivation and Mott-Schottky analysis
2015
The passive behaviour of Alloy 31, a highly-alloyed austenitic stainless steel (UNS N08031), has been investigated in a LiBr heavy brine (700 g/l) at different temperatures using potentiostatic polarisation and Mott-Schottky analysis. Cation vacancies have been found to be the dominant defect in the passive films formed on Alloy 31. An increase in temperature enhanced the generation of cation vacancies at the film/solution interface and raised the steady-state passive current density. The density of defects within the passive film also increased significantly with temperature, making the film more conductive and less protective against localised attacks.
Comparison of the effect of non-polluted and underwater-volcano-polluted seawater on the corrosion resistance of different stainless steels
2015
This work compares the effect of non‐polluted and underwater‐volcano‐polluted seawater on the electrochemical behavior of two different alloys, notably an austenitic stainless steel (SS) and a duplex stainless steel. Polarization measurements, potentiostatic passivation tests, electrochemical impedance spectroscopy and capacitance measurements were performed. Results show that the composition of the polluted seawater negatively affects the passivation kinetics of both AISI 316 SS and Alloy 900, decreasing the corrosion resistance of both alloys. Additionally, when both steels are compared, it can be concluded that passive films formed on Alloy 900 presented better protective properties than…